PA White Basecoat BA.2292(N)

PA White Basecoat BA.2292(N) based on polyaspartic technology formulated specially for spraying application. PA White Basecoat BA.2292(N) provides a short time for sanding, ideas for less time and less step application, suitable for white color.

High solid content for smooth surface & high-gloss finish
Provide good whiteness and opacity
High hardness and scratch resistance
Quick dry and long pot life
Outstanding water resistance

SKU: BA.2292(N) Categories: PA SEALER, PA WOOD COATING

Description

Products' information

Categories	Data
Specific Gravity at temperature 27-37°C	1.35 – 1.65 g/cm³
Solid Content(%)	40 – 70 %
Viscosity: At temperature from 27 to 37°C and air humidity ≤ 70%	30 – 60 secs (Cup Iwata NK02)
Binder Type	Polyaspartic

	Data
Application Method	Spray
Application Temperature	27°C – 37°C
Touch-dry Time (27-37°C)	30 – 45 mins
Hard-dry Time (27-37°C)	18 – 24 hours
Shelf life	6 months from date to manufacture
Reservation in a cool ventilated room at temperature	5°C – 40°C
Theoretical Coverage (gr/m2)	80 – 100 (Depends on the smoothness level of wood surface)
Preparation Instruction	Product surfaces must be clean, dry and flat, smooth not to stick to oil, grease, dirt. Sanding if necessary, then to wipe dust before spraying paint.
Coating System	Spray 3 coats of PA White Basecoat BA.2292-SL with hardener, then spray 2 coats of PA Clear Topcoat BA.2402-BK with hardener.
Mixing Ratio	A : B : Thinner = 2 : 1 : 1

Firm Properties	Result
Touch-dry Time	30 – 45 mins
Hard-dry Time	18 – 24 hours
Sanding	60 – 90 minutes
Pot – life	4- 6 hours
Adhession	5B
Flexibility	≤ 2mm Mandrel
Impact	≥ 45cm
Hardness	—

Controlled materials in the wet paint	Concentration
Aromatic Hydrocarbon	0 mg/kg
Halogenated Compound	0 mg/kg
Formaldehyde	0 mg/kg
Mercury	0 mg/kg
Lead	0 mg/kg
Cadmium	0 mg/kg
Chromium	0 mg/kg
Total Volatile Organic Content (TVOC)	< 500 g/L