Tiếng Việt
UV FILLER SEALER URL6703
- Self cross-linking, rapid curing
- Excellent sanding ability
- Outstanding water resistance
- Excellent adhesion on substrates
- Good resistance to UV irradiation
- Outstanding ability to high-light wood-grain pattern (for transparent coating)
- Excellent fungus resistance
- High hardness and scratch resistance
- High solvent resistance
Products' information
| Categories | Data |
|---|---|
| Specific Gravity at temperature 27-37°C | 1.30 – 1.35 g/cm³ |
| Solid Content(%) | 95 – 100% |
| Viscosity: At temperature from 27 to 37°C and air humidity ≤ 70% | 6000 – 7000 cps Brookfield |
| Binder Type | Oligomer urethane acrylate |
| Data | |
|---|---|
| Application Method | Rolling |
| Application Temperature | 18°C – 40°C |
| Touch-dry Time (27-37°C) | Drying through UV lamp |
| Hard-dry Time (27-37°C) | Drying through UV lamp |
| Shelf life | 6 months |
| Reservation in a cool ventilated room at temperature | 5°C – 40°C |
| Theoretical Coverage (m2/L) | 30 – 35 (Depends on the smoothness level of wood surface) |
| Preparation Instruction | Product surfaces must be clean, dry and flat, smooth not to stick to oil, grease, dirt. Sanding if necessary, then to wipe dust before rolling paint. |
| Coating System | Rolling 1 coat of UV Filler Sealer URL6703, followed by 1 coat of UV Sealer URL6107, followed by 1-2 coat of UV Clear Satin URL6406-10%. |
| Mixing Ratio | Ready for use |
| Firm Properties | Result |
|---|---|
| Touch-dry Time | Drying through UV lamp |
| Hard-dry Time | Drying through UV lamp |
| Adhession | 100 mm2. No Detachment. |
| Flexibility | ≤ 2mm Mandrel |
| Impact | ≥ 45cm |
| Hardness | 2H – 3H |
| Controlled materials in the wet paint | Concentration |
|---|---|
| Aromatic Hydrocarbon | 0 mg/kg |
| Halogenated Compound | 0 mg/kg |
| Formaldehyde | 0 mg/kg |
| Mercury | 0 mg/kg |
| Lead | 0 mg/kg |
| Cadmium | 0 mg/kg |
| Chromium | 0 mg/kg |
| Total Volatile Organic Content (TVOC) | < 200 g/L |